HOME Products Surfece Treatment SiC coated graphite PERMA KOTE™

SiC coated graphite PERMA KOTE™

High-temperature gas-cooled reactors
PERMA KOTE™ is a product created by coating the surface of highly purified isotropic graphite with a fine layer of silicon carbide by means of a proprietary Toyo Tanso Chemical Vapor Deposition (CVD) process.

MOCVD Susceptor
 

Special Graphite

Reflector(Single crystal silicon
manufacturing equipment)

Special Graphite

Pancake susceptor

Pancake susceptor

Barrel susceptor

Barrel susceptor

Characteristics

  • The silicon carbide layer has excellent oxidation resistance, corrosion resistance and chemical resistance.
  • The silicon carbide layer is stable at high temperatures and is extremely hard.
  • Prevents the parting and scattering of graphite particles, and the emission of gas and impurities from the graphite substrate.
  • Both the graphite substrate and silicon carbide layer are of high purity.
  • Both the graphite substrate and silicon carbide layer have a high thermal conductivity, and excellent heat distribution properties.
  • Material is designed so that cracks and delamination do not occur.

Application

  • Susceptor for silicon epitaxial growth
  • Single crystal silicon manufacturing equipment
  • MOCVD susceptors
  • Heaters
  • Heat spreaders
  • Oxidation resistance components

Coating Thickness

Coating Thickness
The standard thickness is 120 μm; however this can be modified within a range of 20 to 500 μm.

Properties/Test Data

Corrosion Resistance

Name Chemical formula Concentration（％） Temperature（℃) Time（h） Change in mass（g/m2）
Hydrofluoric acid HF 47 80 144 -1.0
Hydrochloric acid HCｌ 36 Boiling point 144 0
Sulfuric acid H2SO4 97 110 144 0
Nitric acid HNO3 61 Boiling point 144 0
Hydrofluoric acid + nitric acid HF+HNO3 (1:1） 100 80 288 -1.0
Nitric acid + sulfuric acid HNO3+H2SO4　(1:1） 100 25 288 -1.0
Sodium hydroxide NaOH 20 80 288 0
Phosphoric acid H3PO4 100 100 192 -1.0
Nitrohydrochloric acid HCｌ+HNO3 (3:1) 100 80 192 0

Reactivity with various substances (in a vacuum)

Reactant Chemical Formula 1200℃×3h 1600℃×3h
Aluminum Al ○ △
Boron B ◎ ◎
Cobalt Co △ ×
Chromium Cr △ ×
Copper Cu ○ △
Iron Fe × ×
Molybdenum Mo ◎ ○
Nickel Ni ◎ ×
Lead Pb △ ×
Silicon Si ◎ ○
Tin Sn ◎ △
Tantalum Ta ◎ ◎
Titanium Ti ◎ ○
Vanadium V ◎ ×
Tungsten W ◎ ○
Alumina Al2O3 ◎ ×
Boron oxide B2O3 ◎ ◎
Chromium oxide (Ⅲ) Cr2O3 ◎ ×
Iron oxide (Ⅲ) Fe2O3 × ×
Magnesium oxide MgO ◎ △
Manganese oxide (Ⅳ) MnO2 ◎ ×
Lead oxide(Ⅱ) PbO ○ △
Silicon oxide SiO2 ◎ △
Titanium oxide (Ⅳ) TiO2 ◎ ○
Vanadium oxide (Ⅴ) V2O5 ◎ △
Zirconium oxide (Ⅳ) ZrO2 ◎ ○

◎...No reaction ○...Slight reaction
△...Reaction ×...Significant reaction

Layer Properties

Crystal structure
β-SiC (Cubic system) Structure
β-SiC(Cubic system) Structure
Bulk density 3.2 Mg/m3
Decomposition Temperature 2700℃ or higher
Hardness 2800HK
Electrical Resistivity 0.2 Ω・m （through the fall-of-potential method)
Flexural Strength 170 MPa (through 3-point bending)
Young's Modulus 320 GPa (through the deflection method)

Impurity analysis example mass ppm

Element Content
B 0.15
Na 0.02
Al 0.01
Cr < 0.1
Fe 0.02
Ni < 0.01

*Measurement method: Glow Discharge Mass Spectrometry
*The figures above are measurement examples and are not to be guaranteed.